Pengaruh Komposisi Serat Wlingi (Mansaiang) Terhadap Sifat Kekuatan Tarik

Sutrisno Sutrisno

Abstract


Abstract— The purpose of this study was to determine the effect of the composition of the material using the wlingi fiber fraction with polyester resin on tensile strength. The materials used in this study were Wlingi fiber and BQTN polyester resin. Making was done by hand lay up process. After reaching the desired holding time, the mold is put into the oven and processed and the specimen is removed from the mold. After obtaining four specimens of wlingi fiber variations, the tensile strength testing process was carried out according to ASTM 638. The results of this test indicate that the composition of the material with a wlingi fiber weight fraction of 40% Tensile strength of 118.76 MPa, a strain of 1.32 mm / mm, and a modulus of elasticity of 12355 MPa.

 

Keywords—: tensile strength; wlingi fiber; BQTN resin.

Full Text:

PDF

References


Annual Book of ASTM Standards. 2003. “Annual Book of ASTM standart”. West Conshohocken.

Anonim, 2010, Overview of Composite Processes, ACMA (American Composite Manufacturers Association) Available Online at www.acmanet.org

Anuar H., Ahmad, S.H., Rasid, R., and Zakaria, S., 2005, Tensile Behavior and Morphological Studies of TPNR-KF-CF Hybrid Composite, American Journal of Applied Science (Special Issue): 34-39.

Berthelot J.M., 1984, Composite Materials Mechanical Behavior and Structural and Analysis, Valloise, France.

Billmeyer, Fred W., 1984, Texbook of Polymer Science. Singapore : John Wiley & Sons (SEA) Pte. Ltd.

Bismarck, A., Askargorta, I.A., Lamphe, T., Wielaye, B., Stamboulis, A., Skenderovich, I., and Limbach, H.H., 2002, Surface Characterization of Flax, Hemp and Cellulose Fibres: Surface Properties and the Water Uptake Behavior, Polymer Composite Vol 23, no. 5. of Kenaf Fibers, 16TH International Conference on Composite Materials, Kyoto.

Diharjo, K., Jamasri, Soekrisno, dan Rochardjo, H.S.B., 2006, Kajian Sifat Fisis-Mekanis dan Akustik Komposit Serat Kenaf-Polyester dengan Core Kayu Sengon Laut, Hasil Riset Pendahuluan – Dissertasi, Pascasarjana, UGM, Yogyakarta.

Diharjo, K., Masykuri, M., Budi, L., dan Gunadi, A., 2007, Rekayasa dan Manufaktur Bahan Komposit Sandwich Berpenguat Serat Kenaf Dengan Care Limbah Kayu Sengon Laut Untuk Komponen Gerbong Kereta Api. Lembaga Penelitian dan Pengabdian Masyarakat, Universitas Sebelas Maret, Surakarta.

Eichhorn S.J., Baillie, C.A., Zafeiropoulos, N., and Mwaikambo, L.Y., 2001, Review Current International Research into Selullosic Fibres and Composite, Journal of Materials Science, pp. 2107-2131.

Gibson, O.F., 1994, Principle of Composite Materials, McGraw Hill Company, New York, USA.

Jones R. M., 1999, Mechanics of Composite Materials, McGraw Hill, New York.

Khanam, P.N., Reddy, G.R., Raghu, K., and Naidu, V.S., 2010, Tensile, Flexural, and Compressive Properties of Coir/Silk Fiber-Reinforced Hybrid Composites, Journal of Reinforced Plastic and Composite, Vol. 29, No 14.

Malau, V., dan Widyaparaga, A., 2008, Pengaruh Perlakuan Panas Quench Dan Temper Terhadap Laju Keausan, Ketangguhan Impak, Kekuatan Tarik dan Kekerasan Baja Xw 42 Untuk Keperluan Cetakan Keramik, MEDIA TEKNIK, Tahun XXX, No. 2.

Mishra, S., Misra, M., Triphati, M., Nayak, S., and Mohanty, A., 2000, Potentiality of Pineapple Leaf Fiber as Reinforcement in PALF-Polyester Composite: Surface Modification and Mechanical Performance, J Reinf Plast Compos 20 (4):321-324.

Reddy, G.V., Naidu, S.V., and Rani, S.T.., 2008, Kapok/Glass Polyester Hybrid Composite: Tensile and Hardness Properties, Journal of Reinforced Plastic and Composite, Vol. 27, No 16-17.

Schwartz, M.H., 1984, Composite Material Handbook, McGraw Hill, New York.

Surdia, T., dan Saito, S., 1985. Pengetahuan Bahan Teknik. Dainippon Gita Karya Printing. Jakarta.

Liu, X.Y., and Day. G.C., 2007. Surface Modification And Micromechanical Properties OfJute Fiber Mat Reinforced Polypropylene. State-Key Laboratory of Chemical Engineering, East China University of Science and Technology, 130 Meilong Road, Shanghai 200237, P. R. China.

Yousif, B.L, Leong, O.B., Ong, L.K., and Jye, W.K., 2009, The Effect of Treatment on Tribo-Performance of CFRP Composite, Recent Patents on Materials Science 2009, 2, 67-74s.




DOI: https://doi.org/10.33319/piltek.v6i1.71

Refbacks

  • There are currently no refbacks.



Indexed By :

 

Publisher :

LPPM Universitas Merdeka Madiun
Website: http://unmermadiun.ac.id
Email: lppm@unmer-madiun.ac.id / pilarteknologi@unmer-madiun.ac.id  
© Copyright 2021 PILAR TEKNOLOGI : Jurnal Teknik (Jurnal Ilmiah Ilmu-Ilmu Teknik)
ISSN 2580-3557 (Online)