The Analisa Pengaruh Variasi Waktu Penahanan Panas Dengan Proses Normalizing Pada Baja ST 41 Terhadap Kekerasan Dan Struktur Mikro Effect Of Time On Strength And Elements In ST 41 Steel

Keywords:
Copyright and Licensing:
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Budiman Budiman

a:1:{s:5:"en_US";s:26:"Universitas Merdeka Madiun";}

Abstract

The normalizing heat treatment process was carried out on ST 41 steel, a medium carbon type steel at 850°C heating with variations in holding time of 15 minutes, 20 minutes and 25 minutes with air cooling media. This study determines the hardness and microstructure variations in holding time using air cooling media. The result of this study indicates that the (holding time) factor effect the hardness value, the indentation trace's depth value, and the research specimen's microstructure. The first specimen using a holding time of 15 minutes has a hardness value of 68, 25 HRB with an indentation depth of 0,063 mm. The specimen with a holding time of 20 minutes has a hardness value of 70 HRB with an indentation depth 0,058 mm, and a specimen with a holding time 25 minutes has a hardness value of 68 HRB with an indentation depth of 0,063 mm. The hardness test result found that the specimens with variations in holding time 25 minutes had a smaller hardness value and a deeper depth than variations in holding time of 15 minutes and 20 minutes. Furthermore in the microstructure of specimens with a holding time of 25 minutes, the ferrite phase was more dominant than specimens with holding time of 15 minutes and 20 minutes. The phase that appeared at the holding time of 25 minutes was 80,367 % ferrite phase and 19,633 % pearlite phase. So at a holding time of 25 minutes, the ferrite phase is more dominant, so the hardness value of ST 41 steel decreases.

Downloads

Download data is not yet available.

ASTM Standard E18 – 97a. Standar Test Methods For Rockwell Hardness and Rockwell Superficial Hardness Of Metallic Materials. ASTM International. United States Of America. Page 1 – 14.

ASTM Standard Test Methods For Determining Average Grain Size. ASTM International United States Of America. Page 1 – 26.

Callister William D. Jr. 2007. Materials Science and Engineering. New York : The University of Utah. Adobe PDF eBook.

F. Tambunan Willson, Untung Budiarto, Ari Wibawa Budi Santosa. 2019. “Analisis Kekuatan Tarik, Kekuatan Puntir, Kekerasan, dan Mikrografi Baja ST 60 Sebagai Bahan Propeller Setelah Proses Normalizing dengan Variasi Waktu Penahanan Panas (Holding Time)”. Jurnal Teknik Perkapalan, Vol. 7, No.2, April 2019.

Gary Marhaindra dan Sutiyoko. 2014. “Perubahan Sifat Mekanik Material Karena Perbedaan Konsentrasi Larutan Garam NaCl Pada Proses Quenching” Jurnal Foundry,Vol. 4, No. 1, April 2014.

Handoyo Yopi. 2015. “Pengaruh Quenching dan Tempering Pada Baja S45C Terhadap Sifat Mekanik dan Struktur Mikro Crankshaft”. Jurnal Ilmiah Teknik Mesin, Vol. 3, No.2, Agustus 2015.

Joko Purnomo Dwi, Sarjito Jokosisworo, Untung Budiarto. 2019. “Analisa Pengaruh Holding Time Tempering Terhadap Kekerasan, Keuletan, Ketangguhan, dan Struktur Mikro Pada Baja ST 70”. Jurnal Teknik Perkapalan, Vol. 7, No. 1, Januari 2019.

Jokosisworo Sarjito. 2018. “Pengaruh Normalizing Dengan Variasi Waktu Penahanan Panas (Holding Time) Terhadap Sifat Mekanik Baja ST 46”. Jurnal Ilmu Pengetahuan dan Teknologi Kelautan, Vol. 15, No. 2, Juni 2018.

Mizhar dan Suherman. 2011.” Pengaruh perbedaan Kondisi Tempering Terhadap Struktur Mikro Dan Baja AISI 4140”. Jurnal Dinamis, Vol. 2, No. 8, Januari 2011.

Nofri Media, Acang Taryana. 2017. “Analisis Mekanik Baja SKD 61 Dengan Baja ST 41 Dilakukan Hardening Dengan Variasi Temperatur”. Jurnal Bina Teknika, Vol. 13, No. 2, 2017. Nugroho Stevanus Arie, Totok Yulianto, Septia Hardi Sujiatanti. 2017. “Analisis Pengaruh Cooling Rate pada Material ASTM A36 Akibat Kebakaran Kapal Terhadap Nilai

Kekuatan, Kekerasan dan Struktur Mikronya”. Jurnal Teknik ITS, Vol. 6, No. 1, 2017.

Sardi Vicky Bhaskara, Sarjito Jokosisworo, Hatono Yudo. 2018. “Pengaruh Normalizing dengan Variasi Waktu Penahanan Panas (Holding Time) Baja ST 46 terhadap Uji Kekerasan, Uji Tarik, dan Uji Mikrografi”. Jurnal Teknik Perkapalan, Vol. 6, No. 1, Januari 2018.

Suhardan dan R. Kohar. 2019. “Pengaruh Variasi Temperatur Normalizing Terhadap Besar Butir Dan Kekerasan Material Baja Karbon AISI 1035”. Jurnal Teknik Mesin, Vol. 2, No. 2, Desember 2019.

Team Dosen KBK Teknik Material. 2014. Buku Panduan Praktikum Uji Logam. Jurusan Teknik Mesin Fakultas Teknik Universitas Merdeka Malang.

Widodo Edi, Miftahul Huda. 2016. “Optimasi Holding Time Untuk Mendapatkan Kekerasan Baja S 45 C”. Jurnal R.E.M ,Vol. 1, No.1, 2016.

Title The Analisa Pengaruh Variasi Waktu Penahanan Panas Dengan Proses Normalizing Pada Baja ST 41 Terhadap Kekerasan Dan Struktur Mikro
Issue: Vol. 7 No. 2 (2022): JURNAL PILAR TEKNOLOGI
Section Articles
Published: Nov 30, 2022
DOI: https://doi.org/10.33319/piltek.v7i2.141
Keywords: ST 41 steel, holding time, hardness, normalizing, microstructure.
Author Budiman Budiman
a:1:{s:5:"en_US";s:26:"Universitas Merdeka Madiun";}
 PDF
How to Cite
[1]
Budiman, B. 2022. The Analisa Pengaruh Variasi Waktu Penahanan Panas Dengan Proses Normalizing Pada Baja ST 41 Terhadap Kekerasan Dan Struktur Mikro: Effect Of Time On Strength And Elements In ST 41 Steel . JURNAL PILAR TEKNOLOGI Jurnal Ilmiah Ilmu Ilmu Teknik. 7, 2 (Nov. 2022), 26–31. DOI:https://doi.org/10.33319/piltek.v7i2.141.
 view Abstract : 156      Downloads : 176