Analisis Komposit Serat Daun Pandan Alas Dan Serbuk Kayu Jati Dengan Resin Polyester Terhadap Kekuatan Tarik Dan Daya Serap Air Analisis Komposit Serat Daun Pandan Alas

Keywords:
Copyright and Licensing:
Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

Suryono Adi Waluyo

a:1:{s:5:"en_US";s:28:"Merdeka University of Madiun";}

Wahidin Nuriana

Mustafa

Abstract

Abstract— Pandanus fiber and teak sawdust were waste products that were abundant in availability, but have not been used optimally. Base pandanus fiber and teak sawdust were used as alternative reinforcement for composite materials. The purpose of this study was to test the tensile strength and water absorption of composites reinforced with base pandan fiber and teak sawdust with polyester resin as a matrix. This composite was made by hand lay up technique with variations in the volume fraction of coconut fiber fibers of 10%, 20%, 30%, 30%, 20%, 10% teak sawdust, 60% polyester resin with random fiber orientation, 30 mm fiber length. Composite specimens were cut according to ASTM D 638-01 standards for tensile testing and ASTM D 570 for water absorption tests. The results of this study were tensile strength, strain, modulus of elasticity with optimum strength respectively 30.28 MPa (volume fraction 30%; 10%; 60%), 1.508 mm / mm (volume fraction 10%; 30%; 60%) , 447.46 Mpa (volume fraction 10%; 30%; 60%). Water absorption was 2.07% (volume fraction 10%; 30; 60%).
 
 

Downloads

Download data is not yet available.

Anonim.,2003. Teknologi Disain dan Peralatan Pengolahan Mendong sebagai Bahan Baku Industri Kerajinan.Balai Besar Industri Kerajinan dan Batik.Yogyakarta.

Aris Cholid.B.P., 2013, Studi kuat tekan, kuat geser, dan kuat lekat campuran serbuk gergaji, serbuk ketam dan serbuk amplasan kayu jati dengan perekat resin dan hardener sebagai perbaikan kayu, Fakulitas Teknik, Universitas Sebelas Maret Surakarta.

ASTM., 2003, Annual Book of ASTM Standard.West Conshohocken.

Citra Mardatillah Taufik, Astuti., 2014 Sintesis dan karakterisasi sifat mekanik serta struktur mikro komposit resin yang diperkuat serat daun pandan alas ( pandanus dubius ).

Doraiswarmy et al,.1993 Pineapple LeafFibres, Textile Progress Vol. 24 Number 1,Textile Institute.

Franklin Donald Izaak, Fentje A. Rauf, dan Romels Lumintang., 2013,Analisis sifat mekanik dan daya serap air material komposit serat rotan.

Gapsari F., Setyarini P. H. , 2010, Pengaruh Fraksi Volume Terhadap Kekuatan Tarik Dan Lentur Komposit Resin Berpenguat Serbuk Kayu, Jurnal Rekayasa Mesin Vol.1, No. 2 Tahun 2010 : 59-64, Teknik Mesin, Universitas Brawijaya.

Gibson, Ronald., 1994Principle of composite material, New York: Mc Graw Hill.

Harper, Charles., 1996, Handbook of plastic Elastomers, and Composites.

HartomoA.J, Rusdiharsono D., Hardjanto., 1992 memahami polimer dan perekat, Andi offset, Yogyakarta.

Jones, R.M., 1975 Mechanics Of CompositeMaterial, Hemisphere Publising Co.,New York.

Kirby., 1963 Vegetable Fibres, Leonard Hill,London.

La Ode Mamur, Muhammad Hasbi, Prinob Aksar, 2016, Kajian Eksperimental Sifat Mekanik Material Komposit Serat Tangkai Sagu Dipadukan Dengan Serbuk Gergaji Kayu Jati, Fakultas Teknik Halu Oleo.

Mastur, dan khanif setiyawan., 2016, pengaruh komposit serat pandan samak terhadap kekuatan tarik dan bending pada material bodi kendaraan, Teknik Mesin STT Wiworotomo Purwokerto.

Purba, dan Evri Yani., 2013, Pemanfaatan serat daun pandan duri sebagai campuran dalam peningkatan karakteristik genteng beton.

Matthews, F.L, dan Rawlings, RD., 1993, Composite Material Engineering AndScience, Imperial College Of Science, Technology And Medi-cine, London, UK.

Michael, Elmer Surya, dan Halimatuddahliana., 2013, daya serap air dan kandungan serat ( fiber content ) komposit polyester tidak jenuh (unsaturated polyester) berpengisi serat tandan kosong sawit dan selulosa, departemen Teknik Kimia, Fakulitas Teknik, Universitas Sumatera Utara.

Muslim shares.“Mesh, Definisi dan Konversi ke Millimeter”.

Paryanto Dwi Setyawan., Nasmi Herlina Sari., Dewa Gede Pertama Putra., 2012, pengaruh orientasi dan fraksi volume serat daun nanas (ananas comocuc) terhadap kekuatan tarik komposit polyester tak jenuh ( up ).

Purba, dan Evri Yani., 2013, Pemanfaatan serat daun pandan duri sebagai campuran dalam peningkatan karakteristik genteng beton.

Schwartz M.H., 1984 Composit material Handbook, McGraw Hill, New York..Macmillan publishing company, New York, USA.

Surdia., 1995, Pengetahuan Bahan Teknik,FT,Pradnaya Paramita, Jakarta.

Tumpal Ojahan R., Hansen Aditia M.S., 2015, Analisis Fraksi Volume Serat Pelepah Batang Pisang Bermatriks Unsaturated Resin Polyester (UPR) Terhadap Kekuatan Tarik dan SEM 6(1) :43-48

Title Analisis Komposit Serat Daun Pandan Alas Dan Serbuk Kayu Jati Dengan Resin Polyester Terhadap Kekuatan Tarik Dan Daya Serap Air
Issue: Vol. 7 No. 1 (2022): JURNAL PILAR TEKNOLOGI
Section Articles
Published: Jun 7, 2022
DOI: https://doi.org/10.33319/piltek.v7i1.117
Keywords: Keywords—: base pandanus fiber; teak wood powder; polyester resin; tensile strength; water absorption.
Author
  • Suryono Adi Waluyo
    a:1:{s:5:"en_US";s:28:"Merdeka University of Madiun";}
  • Wahidin Nuriana
  • Mustafa
 PDF
How to Cite
[1]
Adi Waluyo, S., Nuriana, W. and Mustafa 2022. Analisis Komposit Serat Daun Pandan Alas Dan Serbuk Kayu Jati Dengan Resin Polyester Terhadap Kekuatan Tarik Dan Daya Serap Air: Analisis Komposit Serat Daun Pandan Alas. JURNAL PILAR TEKNOLOGI Jurnal Ilmiah Ilmu Ilmu Teknik. 7, 1 (Jun. 2022), 11–17. DOI:https://doi.org/10.33319/piltek.v7i1.117.
 view Abstract : 93      Downloads : 156